CAD/CAM system influence marginal fit of different ceramic types?

Objective: This study aimed to evaluate the marginal fit of zirconia and lithium disilicate ceramic restorations processed by computer-aided design (CAD)/computer-aided manufacturing (CAM) system. Materials and Methods: Ten models were prepared from a metal die, on which scanning was carried out to obtain the virtual model for the processing of zirconia and lithium disilicate ceramics using the CAD/CAM technique. Gypsum models were fabricated and used for scanning the restorations. The infrastructures were designed using software, and CAD/CAM was used to fabricate the restorations (n = 10). The analysis of the marginal discrepancy was measured at 12 points of the margin using the original metallic die. For each crown, an arithmetic average of the discrepancy values was obtained. Results: The marginal fit of the copings of lithium disilicate was 133.10 ± 26.87 μm and zirconia was 127.34 ± 47.97 μm. There was no statistically significant difference (P = 0.7709) between the materials. Conclusion: The marginal fit is similar between lithium disilicate and zirconia ceramics milled in the CAD/CAM system used.

Caracterização in vitro de um novo sistema de resina composta de laboratório / In vitro characterization of a new laboratory composite resin

Objetivo: este estudo caracterizou algumas propriedades de uma resina composta de processamento laboratorial (Resilab, Wilcos do Brasil), indicada para confecção de coroas com e sem metal, pontes anteriores e posteriores, inlays, onlays e facetas laminadas. Metodologia: as propriedades avaliadas foram rugosidade superficial, dureza, resistência à flexão, resistência adesiva a três ligas metálicas (Au, NiCr e CoCr) e microinfiltração da interface resina/metal. Todos os espécimes foram submetidos a dois ciclos de polimerização, conforme instruções do fabricante. Dez espécimes circulares (4x3 mm) foram preparados para os testes de dureza (VHN) e rugosidade superficial (Ra). A resistência flexural em três pontos (MPa) foi medida a partir de espécimes retangulares (10x5x2 mm), sob velocidade de 1 mm/min. Os ensaios que envolveram ligas metálicas (resistência adesiva e microinfiltração) foram submetidos à análise estatística (p<0,05) (Anova, Tukey, Kruskal-Wallis). Resultados: não houve diferenças entre as médias de resistência de união. Quanto à infiltração marginal, o grupo CoCr diferiu dos grupos Au e NiCr em espécimes sem retenção mecânica e submetidos a ciclagem térmica. Conclusão: considerando os resultados deste estudo in vitro e a literatura pesquisada, o sistema Resilab mostrou comportamento satisfatório quanto às propriedades estudadas. A resistência de união não dependeu da liga metálica utilizada.

Aim: this study aimed to determine some of the properties of a laboratory composite indicated for metallic and non-metallic crowns, anterior and posterior bridges, inlays, onlays and laminate veneers. Methology: the properties evaluated were surface roughness, flexural strength, shear bond strength to three metal alloys and the microleakage at the composite/ metal interface. All specimens were subjected to cycles of polymerization, according the manufacturer instructions. Ten round specimens (4x3 mm) were prepared for hardness (VHN) and surface roughness tests (Ra). The three-point flexural strength was measured on rectangular shaped specimens (10x5x2 mm), at 1 mm/min speed. The experiments involving dental alloys (bond strength and microleakage) were submitted to statistical analysis (p<0, 05) (Anova, Tukey, Kruskal-Wallis). Results: there were no statistically significant diferences between the bond strength means. As for the marginal leakage, the CoCr group differed of the Au and NiCr groups in specimens without mechanical retention and subjected to thermocycling. Conclusion: according to our results and the literature search, the Resilab system showed satisfactory performance regarding the properties evaluated. The bond strength was not dependable on the metal alloy used.

The adhesive system and root canal region do not influence the degree of conversion of dual resin cement

OBJECTIVES: The aim of this study was to evaluate the influence of two adhesive systems and the post space region on the degree of conversion of dual resin cement and its bond strength to root dentin. MATERIAL AND METHODS: One three-step etch-and-rinse (All-bond 2, Bisco) and another one-step self-etch (Xeno III, Dentsply) adhesive systems were applied on 20 (n=10) crownless bovine incisors, at 12-mm-deep post space preparation, and a fiber post (DT Light Post, Bisco) was cemented using a dual cure resin cement (Duo-Link, Bisco). Three transverse sections (3 mm) were obtained, being one from each study region (cervical, middle and apical). The degree of conversion of the dual cure resin cement was determined by a micro-Raman spectrometer. The data ( percent) were submitted to repeated-measures analysis of variance and Tukey's test (p<0.05). RESULTS: For both groups, the degree of conversion means ( percent) (All bond 2cervical = 69.3; All bond 2middle = 55.1; All bond 2apical= 56; Xeno III cervical = 68.7; Xeno IIImiddle = 68.8; Xeno III apical = 54.3) were not significantly different along the post space regions (p<0.05). CONCLUSION: Neither the adhesive nor the post space region influenced the degree of conversion of the cement layer.

Comparison of resin push-out strength to root dentin of bovine- and human-teeth.

Aim : To compare the push-out strength of bovine- and human-root dentin and, thus, evaluate the suitability of bovine-root dentin to substitute human-root dentin for bond strength testing. Materials and Methods : Ten single-rooted human-teeth and ten bovine incisors were prepared using a #3 bur of a fiber post system (12 mm long). The posts were duplicated with resin cement (Duolink). The root canals were treated with All Bond 2 adhesive system and the resin posts were cemented using Duolink. The specimens were cut perpendicular to their long axis, yielding disc-specimens with 1.5 mm thickness, which were submitted to a push-out test (1 mm/min). Ten bond strength values per group (n = 10) were used for statistical analysis (Student t test, a =.05). Results : Statistically significant differences were found for the bond strength values between bovine- (4.1 ± 1.3 MPa) and human-root dentin (8.6 ± 5.7 MPa) (P =.0001). Conclusion : The push-out strengths of bovine- and human-root dentin were statistically different.

Adhesive cementation of zirconia posts to root dentin: evaluation of the mechanical cycling effect

This study evaluated the effect of mechanical cycling on the bond strength of zirconia posts to root dentin. Thirty single-rooted human teeth were transversally sectioned to a length of 16 mm. The canal preparation was performed with zirconia post system drills (CosmoPost, Ivoclar) to a depth of 12 mm. For post cementation, the canals were treated with total-etch, 3-steps All-Bond 2 (Bisco), and the posts were cemented with Duolink dual resin cement (Bisco). Three groups were formed (n = 10): G1 - control, no mechanical cycling; G2 - 20,000 mechanical cycles; G3 - 2,000,000 mechanical cycles. A 1.6-mm-thick punch induced loads of 50 N, at a 45° angle to the long axis of the specimens and at a frequency of 8 Hz directly on the posts. To evaluate the bond strengths, the specimens were sectioned perpendicular to the long axis of the teeth, generating 2-mm-thick slices, approximately (5 sections per teeth), which were subjected to the push-out test in a universal testing machine at a 1 mm/min crosshead speed. The push-out bond strength was affected by the mechanical cycling (1-way ANOVA, p = .0001). The results of the control group (7.7 ± 1.3 MPa) were statistically higher than those of G2 (3.9 ± 2.2 MPa) and G3 (3.3 ± 2.3 MPa). It was concluded that the mechanical cycling damaged the bond strength of zirconia posts to root dentin.

Influence of additional polymerization in the microhardness of direct composite resins/Influência da polimerização adicional na microdureza de resinas compostas diretas

Objective: To evaluate different methods of additional polymerization in the VickersÆ microhardness of three composite resins. Material and Methods: With assistance of a metallic matrix (3 x 4mm), 30 specimens (sps) of each direct resincomposite (drc) were prepared, entitled: Filtek Z250(3M ESPE, Saint Paul/MN-USA)(Gr1), W3D(Wilcos, Petrópolis/RJ-Brazil)(Gr2), and EstheticX (Dentsply/York/PA-USA)(Gr3). All sps were photopolimerized, by the incrementaltechnique, during 40 seconds (Gr1 - n=10: control). After that, 20 samples of each group were divided and half of thesamples (n=10) were submitted to the additional polymerization during 15 minutes to 127ºC in autoclave (Gr2) and theother half in stove (Gr3). After all sps were stored in distilled water (37ºC/24 hours). The microhardness was accomplishedin digital machine (Future-Tech, FM 700 Model), with 50kg of load. The data obtained (Kg/mm2) were analyzedutilizing the ANOVA Test (2 factors) and Tukey test (p<0.05). Results: The values of mean ± standard deviations obtainedwere: Gr1a(84,2±5,1), Gr1b (71,6±6,7), Gr1c (89,6±7,4), Gr2a (101,1±6,0), Gr2b (96,4±9,0), Gr2c (112,6±7,3), Gr3a(74,0±6,5), Gr3b (66,0±12,7) e Gr3c (81,7±6,5). The polymerization in stove produced a higher microhardness than theother kinds of polymerization (p<0.05) and the microhardness of the resins statistically differed among them (p<0.05).Conclusion: The additional polymerization of the Filtek Z250 in the stove produced microhardness statistically higherthan the others.

Objetivo: Frente à possibilidade de se utilizar resinas compostas diretas (rcds) para procedimentos restauradores indiretos,o presente estudo propôs avaliar diferentes métodos de polimerização adicional na microdureza VickersÆ de trêsresinas compostas de uso direto. Materiais e Métodos: Com o auxílio de uma matriz metálica (3,0 x 4,0mm), foramconfeccionados 30 corpos-de-prova de cada resina denominadas: W3D(Wilcos/Brasil)(Gr1), Z250(3M ESPE/EUA)(Gr2) e Esthetic X(Dentisply/EUA)(Gr3). Todos os espécimes (sps) foram fotopolimerizados, pela técnica incremental,durante 40 segundos (Gr1 - n=10: controle). Em seguida, 20 amostras de cada grupo foram aleatoriamente divididas emetade das amostras (n=10) submetidas à polimerização adicional durante 15 minutos a 127ºC em autoclave (Gr2) e aoutra parte em estufa (Gr3). Após todos os sps foram armazenados em água destilada a 37ºC durante 24 horas. O testede microdureza foi realizado em microdurômetro (Future-Tech, Modelo FM 700), com força de 50 kg. Os dados obtidos(Kg/mm2) foram analisados utilizando o teste ANOVA (2 fatores) e o teste t (Tukey) (p<0.05). Resultados: Os valores demédias±desvios padrões obtidos foram: Gr1a(84,2±5,1), Gr1b (71,6±6,7), Gr1c (89,6±7,4), Gr2a (101,1±6,0), Gr2b(96,4±9,0), Gr2c (112,6±7,3), Gr3a (74,0±6,5), Gr3b (66,0±12,7) e Gr3c (81,7±6,5). Observou-se que a polimerizaçãoem estufa gerou maior microdureza que as demais polimerizações (p<0,05) e que a microdureza das resinas diferiuestatisticamente entre si (p<0,05). Conclusão: Dessa forma, é lícito concluir que a polimerização adicional da Z250na estufa gerou microdureza estatisticamente superior aos demais grupos.

Eficiência de corte de frezas para implantes / Cut efficiency of implant drills

O objetivo nessa pesquisa foi comparar e eficiência de corte de duas brocas para implantes, de formatos iguais e recobrimentos de superfície diferentes ((B1) com e (B2) sem recobrimento de nitreto de titânio). Para isso, foram utilizadas amostras de osso cortical de fêmur bovino, nas quais foram feitas perfurações (testes “cegos”) por 50 operadores. O teste foi conduzido com velocidade de 1500 rpm e irrigação constante de soro fisiológico. Foram registradas as forças exercidas e o tempo despendido durante perfurações ósseas, comparando seu desempenho entre os diferentes operadores. Os resultados foram submetidos a um teste estatístico de análise de variância Anova e seguidos pelo teste de Tukey 5%. O valor médio de tempo máximo despendido durante a perfuração com a B1(T1= 36,58 s) diferiu do tempo da B2 (T2= 22,2 s)e o valor médio de pressão máxima exercida durante a perfuração com a B1 (P1 = 3,55 kg) diferiu da pressão máxima da B2 (P2 = 3,264 kg). Pode-se concluir que a broca sem o recobrimento de nitreto de titânio apresentou comportamento mais favorável, requerendo menor pressão e menos tempo de perfuração.

Efeito do tempo de condicionamento da superfície cerâmica sobre a resistência / Effect of the conditioning time of the ceramic surface on bond strength between a fluorapatite ceramic and a resin cement

O objetivo deste estudo foi avaliar a resistência de união entre uma cerâmica sintética de fluorapatita e leucita livre de feldspato e um cimento resinoso dual, variando o tempo de condicionamento ácido da superfície da cerâmica. Foram confeccionados 16 blocos de cerâmica (IPS d. SIGN- Ivoclar-Vivadent) que foram divididos aleatoriamente em 2 grupos (n=8), conforme o tempo de condicionamento ácido da superfície cerâmica: G1 - condicionamento durante 30 segundos com ácido fluorídrico 10%, seguido da aplicação do agente silano (Primer ceramic, 3M/Espe); G2: condicionamento com ácido fluorídrico 10% durante 2 minutos, seguido da aplicação do silano (Primer ceramic, 3M/Espe). Os blocos de cerâmica foram unidos a blocos de resina composta, recém confeccionados, (Fill Magic, Vigodent) com o cimento resinoso Rely X (3M/Espe) sob uma carga de 750g. Os conjuntos foram armazenados em água por 24h e seccionados em dois eixos, x e y, obtendo-se corpos-de-prova (CP) com área de aproximadamente 0,7 mm2. Os CP foram submetidos ao ensaio de microtração a uma velocidade de 0,5 mm/min. Os resultados foram submetidos a duas análises estatísticas utilizando todos os CP, incluindo os com valores zero (G1 = 12,99 ± 6,7 MPa e G2 = 14,97 ± 3,7 MPa) e excluindo os com valores zero (G1 = 20,19 ± 3,8 MPa e G2 = 22,31 ± 2,8 MPa). Não foi observada diferença estatística entre os grupos em nenhuma das análises (p>0,05).

Avaliação da resistência adesiva entre uma cerâmica aluminizada e um cimento resinoso submetidos à ciclagem térmica / Effect of the thermocycling on bond strength of an aluminous ceramic to a resin cement

O objetivo este estudo foi avaliar o efeito da ciclagem térmica sobre a resistência adesiva entre a superfície cerâmica do In-Ceram (Vita-Zahnfabrik, bad sãckingen, Alemanha) e o cimento resinoso (Panavia F, Kuraray CO, Japao). Foram fabricados nove blocos cerâmicos com dimensoes de 5X6X6mm. Uma fas faces com 5X6mm de cada bloco cerâmico foi condicionada com uma cobertura triboquímica de sílica (Sistema Rocatec, ESPE- Seefeld - Alemanha) e em seguida cimentada com Panavia F a outro bloco idêntico de resina composta (Cleafil AP-X, Kuraray Co - Japao). Os nove grupos formados por cerâmica, cimento e resina composta foram cortados em 60 corpos-de-prova com dimensoes de 10X1X1mm e área adesiva que apresentava 1mm2+-0,1mm2. Os corpos-de-prova foram divididos em 3 grupos (n=20):G1 - armazenagem durante 14 dias em água destilada a 37ºC; G2 - 6000 ciclos térmicos (5ºC-55ºC, 30s em cada temperatura); G3 - 12000 ciclos térmicos (5ºC - 55ºC, 30s em cada temperatur). Após os condicionamento térmicos, os corpos-de-prova foram fixados com adesivo de cianoacrilato ao dispositivo de microtraçao e testados em uma máquina de ensaio universal (EMIC - DL-1000, Equipamentos e Sistemas Ltda., dos de Sao José dos Pinhais - o PR, Brasil) com velocidade constante sw 0,5mm/min. Os dados foram submetidos aos métodos estatísticos de ANOVA e Tukey. Os resultados indicaram que os valores médios de tensao de rupturas (MPa) de G1 (14,97+-4.68) nao diferiram estatisticamente (p<5porcento) de G2 (12.27+-4.72), porém houve diferença significante entre G1 e G3 (9.89+-4.16). Foi possível concluir que a termociclagem reduziu os valores de resistência adesiva significativamente quando os cors-de-prova foram submetidos a 12000 ciclos.